外墙保温系统中粘结材料的检测技术分析

选择了几份典型的外墙外保温系统标准,通过对这几份标准中胶粘剂和抹面胶浆的成型和检测方法的比较,分析了现有检测技术的优劣,并结合工作实践提出了建议。     

Simultaneous improvement of thermal conductivity and mechanical properties for mechanically mixed ABS/h-BN composites by using small amounts of hyperbranched polymer additives

Recently, thermal interface materials (TIMs) are in great demands for modern electronics. For mechanically mixed polymer composite TIMs, the thermal conductivity and the mechanical properties are generally lower than expected values due to the sharply increased viscosity and poor filler dispersion. This work shows that addition of a small amount of polyester-based hyperbranched polymer (HBP) avoided the trade-off in mechanically mixed ABS/hexagonal boron nitride (h-BN) composites. After adding 0.5 wt% HBP, the maximum h-BN content in the composites increased from 50 to 60 wt%. The out-of-plane, in-plane thermal conductivity, and tensile strength of ABS/h-BN with 50 wt% h-BN were 0.408, 0.517 W/mK, and 18 MPa, respectively, and were increased to 0.729, 0.847 W/mK, and 32 MPa by adding 0.5 wt% HBP, while 0.972, 1.12 W/mK, and 29.5 MPa were achieved for ABS/h-BN/HBP with 60 wt% h-BN. The morphological and rheological results proved that these enhancements are due to the improved h-BN dispersion by decreasing viscosity of composites during mixing. Theoretical modeling based on the modified effective medium theory confirmed such results and showed that the interfacial thermal resistance also decreased slightly. Thus, this work demonstrates a facile and scalable method for simultaneously improving the thermal conductivity and mechanical properties of thermoplastic-based TIMs.     

改进Elman神经网络在短期热负荷预测中的应用

热电厂的短期热负荷预测在城市集中供暖中起着至关重要的作用,直接影响热电厂的经济效益和热能利用率。电厂的短期热负荷一般采用神经网络预测模型进行预测,而BP神经网络应用最为广泛。Elman神经网络算法在BP神经网络基础上加入了承接层,作为一步延时算子,实现记忆能力,使系统具备适应时变能力,增强系统全局稳定性。但Elman神经网络算法模型的构造依然需要大量样本的支撑,而且输入层的变量多,导致预测时间依然很长,收敛速度慢。该文在Elman神经网络预测前,进行了相关系数预处理和对样本中异常值的平均化预处理,通过数据归一化运算,使Elman神经网络输入层变量大幅减少。仿真实验表明,改进的Elman神经网络算法使预测模型快速寻优,减少预测时间的同时明显提高预测精度。     

红外热成像在乳腺疾病检测的应用研究

乳腺疾病已严重危害女性身心健康,其中乳腺癌更位居全球范围内女性癌症发病率和死亡率首位,因此乳腺癌的早期发现意义重大。传统结构影像学早期检测疾病具有一定局限性,而红外热成像作为功能成像技术可为乳腺癌的早期筛查提供有效线索。因此本文主要就红外热成像在乳腺疾病的早期检测及预后评估的应用价值进行综述。     

Fabrication of Cu/graphite film/Cu sandwich composites with ultrahigh thermal conductivity for thermal management applications

Effective thermal management of electronic integrated devices with high powder density has become a serious issue, which requires materials with high thermal conductivity (TC). In order to solve the problem of weak bonding between graphite and Cu, a novel Cu/graphite film/Cu sandwich composite (Cu/GF/Cu composite) with ultrahigh TC was fabricated by electro-deposition. The micro-riveting structure was introduced to enhance the bonding strength between graphite film and deposited Cu layers by preparing a rectangular array of micro-holes on the graphite film before electro-deposition. TC and mechanical properties of the composites with different graphite volume fractions and current densities were investigated. The results showed that the TC enhancement generated by the micro-riveting structure for Cu/GF/Cu composites at low graphite content was more effective than that at high graphite content, and the strong texture orientation of deposited Cu resulted in high TC. Under the optimizing preparing condition, the highest in-plane TC reached 824.3 W·m⁻¹·K⁻¹, while the ultimate tensile strength of this composite was about four times higher than that of the graphite film.     

High-performance NdSrCo2O5+δ–Ce0.8Gd0.2O2-δ composite cathodes for electrolyte-supported microtubular solid oxide fuel cells

NdSrCo₂O_5+δ (NSCO) is a perovskite with an electrical conductivity of 1551.3 S cm⁻¹ at 500 °C and 921.7 S cm⁻¹ at 800 °C and has a metal-like temperature dependence. This perovskite is used as the cathode material for Ce_0.8Gd_0.2O_2-δ (GDC)-supported microtubular solid oxide fuel cells (MT-SOFCs). The MT-SOFCs fabricated in this study consist of a bilayer anode, comprising a NiO–GDC composite layer and a NiO layer, and a NSCO–GDC composite cathode. Three cell designs with different outer tube diameters, GDC thicknesses, and NSCO/GDC ratios are designed. The MT-SOFC with an outer tube diameter of 1.86 mm, an electrolyte thickness of 180 μm, and a 5NSCO–5GDC composite cathode presents the best performance. The flexural strength of the aforementioned cell is 177 MPa, which is sufficient to confer mechanical integrity to the cell. Moreover, the ohmic and polarization resistance values of the cell are 0.22 and 0.09 Ω cm² at 700 °C, respectively, and 0.15 and 0.03 Ω cm² at 800 °C, respectively. These results indicate that the NSCO-GDC composite exhibits high electrochemical activity. The maximum power densities of the cell at 700 and 800 °C are 0.46 and 0.67 W cm⁻², respectively, exceeding those of existing electrolyte-supported MT-SOFCs with similar electrolyte thicknesses.     

生物质纤维和改性木质素对聚乳酸结晶性能的影响

采用改性木质素(MZS)作为成核剂,生物质纤维(BF)作为增强剂,通过双螺杆挤出机制备了生物降解的聚乳酸(PLA)/BF/MZS材料。采用差式扫量热仪(DSC)、电子万能试验机和扫描电子显微镜(SEM)分析了BF和MZS对PLA材料性能的影响。结果表明,BF和MZS有效提高了PLA的结晶能力和力学性能。当BF和MZS的含量分别为15%和1%时,PLA材料结晶度提高至67.1%,在50℃/min降温速率下仍具有较高的结晶能力。105℃等温结晶时,15%BF和1%MZS的PLA材料半结晶时间降低至9.0 s,比纯PLA缩短了72.2%。当PLA含有3%BF和1%MZS时,拉伸强度和冲击强度分别为70.1 MPa和7.4 kJ/m^2,比纯PLA分别提高了7.8%和10.4%,根据SEM显示,当BF含量为3%时,在PLA材料中分布较均匀。     

内燃机活塞环表面处理技术

活塞环在内燃机中有着支撑、密闭、储油、导热的作用,内燃机活塞环制备材料应该具备优良的加工性能、耐高温、耐腐蚀、导热性好且具有良好的强韧性,较好的与气缸材料表面的磨合性能。球墨铸铁和专用钢材已经成为制备内燃机活塞环的基础材料,目前国内外采用多种表面处理技术比如:镀铬、氮化、PVD与CVD镀膜、喷钼、喷涂陶瓷层等表面处理工艺进行表面改性,提高内燃机活塞环的使用寿命和使用性能。需要不断研究和开发新的内燃机活塞环的表面处理技术来满足实际生产和应用中内燃机越来越高的要求。     

高温氢工质热物理性质计算分析

氢工质在新能源与动力、航天推进、化工材料等领域有着广泛应用。通过开展高温氢工质热力学与输运性质研究，建立了原子态氢、分子态氢、热解平衡态氢的热物理性质计算模型，开发了热物性计算程序Prop_H_H2，适用范围为温度100~3 500 K、压力104~5×107 Pa 。验证表明，Prop_H_H2在适用范围内计算氢工质的物性参数合理可靠，在温度200~3 000 K、压力104~107 Pa范围内，程序预测值更加准确，相对偏差在±5%左右。本研究可为氢工质相关的航天推进、应用物理学、能源动力等行业的科研和应用提供支持借鉴。     

回转窑煅烧段烟气最高温度的间接测量

通过对球团回转窑内的热平衡分析,得到回转窑稳定工作时,煅烧段烟气最高温度与窑尾烟气温度之间的理论关系式。该公式表明回转窑在稳定工作时,窑尾烟气温度与煅烧段烟气最高温度存在线性关系。通过三维建模,运用有限元技术对窑尾烟气温度与煅烧段烟气最高温度进行了数值模拟。研究结果可为回转窑煅烧段温度在线监测和自动化调节火焰温度提供理论指导。